• For glass ceramics and zirconia materials, if the surface is finished with porcelain powder and then glazed, the temperature is raised to 710℃, and other factors remain unchanged.
• The above is the recommended sintering curve. There are slight differences in different sintering furnaces. Technicianscan adjust the sintering curve appropriately according to actual conditions.

Features:

*Low temperature sintering

*Extremely simple operation

*Bionic beauty

*Easy to shape

*Precise color

*Good biocompatibility

*Lightweight and simple set, reducing costs

Tips:

1,Before use, the restoration (such as zirconium oxide, glass ceramic) must be thoroughly cleaned to avoid saliva, grease or polishing residue that may affect adhesion. It is recommended to use a special cleaning agent (such as alcohol ultrasonic cleaning).

2,Make sure the restoration is completely dry before staining. A humid environment may cause uneven staining or bubbles to form.

3.Please mix the paste and liquid evenly before daily use to ensure the consistency and operational feel of the paste during use.

4.Please do not pour out the excess glaze liquid in the paste bottle.

5. Each bottle of paste contains glaze ingredients, so there is no need to apply glaze separately.

6. Please make sure to use a clean and dry glaze brush and do not mix water into the paste. lf the water is mixed into the paste, white mist particles will be produced after sintering.

7. During the paste preparation process, add an appropriate amount of diluent and mix thoroughly in a clock wise direction to ensure that there are no bubbles in the paste.

 Case: