Fast-curing versatile elastic adhesive.
With the new concept of "instantaneous elasticity", we meet the needs for short-time bonding.
A one-component moisture-curing / quick-curing type with excellent workability.
It does not contain siloxane that causes contact failure.
Japan Adhesive Industry Association JAIA F ☆☆☆☆ 4VOC standard compliant product.
Has good adhesion to various adherends.
It is a siloxane-free environmentally friendly product.
By taking an open time, even an adherend without water supply can be cured quickly.
Fast curing
Good low temperature curability
Versatile for adhering to a wide range of materials
High durability
Ultra-fast curing type
One-component elastic adhesive
Main component Acrylic modified silicone resin
Appearance black paste
Viscosity Pa · s / 23 ℃ 82.6
Density g / cm3 1.14
Touch drying time 23 ℃ 2.5 minutes
Tension Shear Adhesive Strength MPa 3.2
T-type peeling adhesive strength N / mm 3.31
Hardened Physical Characteristics Hardness Shore D 58
Breaking strength MPa 3.42
Elongation at break% 120
Electrical characteristics Volume resistivity Ω ・ cm 3.5 × 10 (12)
Permittivity 100Hz 6.30
Dissipation factor 100Hz 0.28
Suitable for versatile adhesions that require initial rise strength.
(*) Suitable for adhesion that requires durability such as repeated cooling and heating.
* Open time of about 1 minute after application, handleable time is about 1 to 2 minutes / 23 ° C.
After application, the open time is about 2 minutes, and the handleable time is about 30 seconds to 1 minute / 23 ° C.
Adhesion of metal, hard plastic, rubber, leather, wood, tile, and concrete.