Clear Perm/Remov Two-Sided Laminate (Self-Wound) PG-311
PG-311 is a double-coated pressure sensitive 1.0 mil clear polyester film with permanent adhesive on one side and removable adhesive on the other side. PG-311 is self wound on a 1.25 mil clear polyester liner printed with “Remove to Expose Adhesive” to identify the removable adhesive. This clear liner allows the graphics to be viewed after application of the PG-311 mounting adhesive. This product is designed for laminating thin flexible plastic films and papers commonly found in graphics for temporary application to glass. The permanent adhesive is exposed when the product is unwound leaving the removable adhesive protected by the liner. This clear mounting film can be laminated by the cold laminating process without the addition of heat.
Film Type: Clear Polyester Carrier
Film Thickness: (mils/μm) 1.0 / 25
Dimensional Stability: N/A
Adhesive Type: Solvent Acrylic Adhesive
Thickness (mils/μm): 0.8-1.0 / 20-25
Peel Strength on Stainless Steel (lbf/in) / (N/25mm) 15 min: Remov. Side: 0.02-0.08 / 0.09-0.35 | Perm. Side: 1.0 / 4.4
Peel Strength on Stainless Steel (lbf/in) / (N/25mm) 24 hrs: Remov. Side: 0.04-0.10 / 0.18-0.44 | Perm. Side: 2.1 / 9.2
Peel Strength on Glass (lbf/in) / (N/25mm) 15 min: Remov. Side: 0.05-0.15 / 0.22-0.66
Peel Strength on Glass (lbf/in) / (N/25mm) 24 hrs: Remov. Side: 0.05-0.15 / 0.22-0.66
Liner Weight: (#/gsm): N/A
Liner Type: Clear Polyester, Silicone 2 Sides
Liner Thickness: (mils/μm) 1.2 / 30
Release Force @ 300” / min (g/2”): 15-25
Application Temperature: >+30 °F
Service Temperature: -40 °F to 180 °F
Storage Temp / Rel. Humidity: 70 °F / 50%
Outdoor Durability: 6 Months
Removability: 6 Months
Clear Perm/Remov Two-Sided Laminate (Dual Liner) PG-811
PG-811 is a double-coated pressure sensitive 1.0 mil clear polyester film with a permanent adhesive on one side and a removable adhesive on the other side. PG-811 is a two liner construction. One side has a 1.2 mil clear polyester liner printed with “Remove to Expose Adhesive” to identify the removable adhesive and allows the graphics to be viewed after lamination. The other side has a 1.5 mil clear polyester liner for added clarity and wet out (permanent adhesive side). This product is designed for laminating thin flexible plastic films and papers commonly found in graphics for temporary application to glass. PG-811 clear mounting film can be laminated by a cold laminating process without the addition of heat.
Film Type: Clear Polyester Carrier
Film Thickness: (mils/μm) 1.0 / 25
Dimensional Stability: N/A
Adhesive Type: Solvent Acrylic Adhesive
Thickness (mils/μm): 0.8-1.0 / 20-25
Peel Strength on Stainless Steel (lbf/in) / (N/25mm) 15 min: Remov. Side: 0.02-0.08 / 0.09-0.35 | Perm. Side: 1.0 / 4.4
Peel Strength on Stainless Steel (lbf/in) / (N/25mm) 24 hrs: Remov. Side: 0.04-0.10 / 0.18-0.44 | Perm. Side: 2.1 / 9.2
Peel Strength on Glass (lbf/in) / (N/25mm) 15 min: Remov. Side: 0.05-0.15 / 0.22-0.66
Peel Strength on Glass (lbf/in) / (N/25mm) 24 hrs: Remov. Side: 0.05-0.15 / 0.22-0.66
Liner Weight: (#/gsm) N/A
Liner Type: Remov. Side: clear printed polyester | Perm. Side: clear polyester
Liner Thickness: (mils/μm) Remov. Side: 1.2 / 30 | Perm. Side: 1.5 / 38
Release Force @ 300” / min (g/2”): Remov. Side: 15-25 | Perm. Side: 20-30
Application Temperature: >+30 °F
Service Temperature: -40 °F to 180 °F
Storage Temp / Rel. Humidity: 70 °F / 50%
Clear Perm/Remov Two-Sided Laminate (Dual Liner with Air-Egress) PG-611
PG-611 is a double-coated pressure sensitive 1.0 mil clear polyester film with a high-tack permanent adhesive on one side and a high-tack removable adhesive on the other side. PG-611 has a 4.5 mil clear air egress PET liner printed with “Remove to Expose Adhesive” on the removable adhesive side. This air egress liner assures smooth bubble free application (NOTE: Air-Egress adhesives are DRY APPLY ONLY). The clear liner allows the graphics to be viewed after lamination with PG-611. This product is designed for laminating thin flexible plastic films and papers commonly found in graphics for temporary application to glass. The high-tack permanent HTAP adhesive is protected by a 1.5 mil clear polyester liner. This clear mounting film can be laminated by the cold laminating process without the addition of heat.
Film Type: Clear Polyester Carrier
Film Thickness: (mils/μm) 1.0 / 25
Dimensional Stability: N/A
Adhesive Type: Solvent Acrylic (Remov. Side) / Emulsion Acrylic (Perm. Side)
Adhesive Thickness: (mils/μm) Remov. Side: 0.6-0.08 / 15-20 | Perm. Side: 0.8-1.0 / 20-25
Peel Strength on Stainless Steel (lbf/in) / (N/25mm) 15 min: Remov. Side: 0.5-1.0 / 2.2-4.4 | Perm. Side: 1.0 / 44
Peel Strength on Stainless Steel (lbf/in) / (N/25mm) 24 hrs: Remov. Side: 0.8-1.2 / 3.5-5.3 | Perm. Side: 2.1 / 9.2
Peel Strength on Glass (lbf/in) / (N/25mm) 15 min: Remov. Side: 0.7-1.3 / 3.1-5.7
Peel Strength on Glass (lbf/in) / (N/25mm) 24 hrs: Remov. Side: 0.7-1.3 / 3.1-5.7
Liner Weight: (#/gsm) N/A
Liner Type: Clear Printed Polyester/Air-egress (Remov. Side) / Clear Polyester (Perm. Side)
Liner Thickness: (mils/μm) Remov. Side: 4.5 / 114 | Perm. Side: 1.5 / 38
Release Force @ 300” / min (g/2”): Remov. Side: 55-85 | Perm. Side: 20-30
Application Temperature: >+40 °F
Service Temperature: -40 °F to 180 °F
Storage Temp / Rel. Humidity: 70 °F / 50%
Outdoor Durability: 1 year