Carbon fiber wire high temperature resistant conductive 3K6K12K24K tensile conductive carbon fiber heating wire
model:
3K10 meters
6K10 meters
12K10 meters
24K10 meters
3K100 grams around 500 meters
6K100 grams about 240 meters
12K100 grams about 120 meters
24K100 grams about 60 meters
3K50 grams about 250 meters
6K50 grams about 120 meters
12K50 grams about 60 meters
24K50 grams about 30 meters
6K10 meters
12K10 meters
24K10 meters
3K100 grams around 500 meters
6K100 grams about 240 meters
12K100 grams about 120 meters
24K100 grams about 60 meters
3K50 grams about 250 meters
6K50 grams about 120 meters
12K50 grams about 60 meters
24K50 grams about 30 meters
product description
Carbon fiber yarn is a special fiber composed of carbon elements. It has the characteristics of high temperature resistance, friction resistance, electrical conductivity, heat conduction and corrosion resistance. The appearance is fibrous, soft, and can be processed into various fabrics. Because of its graphite microcrystalline structure is oriented along the fiber axis, it has a high Strength and modulus. Carbon fiber has a low density, so its specific strength and specific modulus are high. The main purpose of carbon fiber is to compound with resin, metal, ceramics and carbon as a reinforcing material to make advanced composite materials.
High-strength, high-modulus fiber with carbon content above 90%. High temperature resistance ranks first among all chemical fibers. It is made of acrylic fiber and viscose fiber as raw materials, after high temperature oxidation and carbonization. It is an excellent material for manufacturing high-tech equipment such as aerospace and aviation.
Carbon fiber yarn is a special fiber composed of carbon elements. It has the characteristics of high temperature resistance, friction resistance, electrical conductivity, heat conduction and corrosion resistance. The appearance is fibrous, soft, and can be processed into various fabrics. Because of its graphite microcrystalline structure is oriented along the fiber axis, it has a high Strength and modulus. Carbon fiber has a low density, so its specific strength and specific modulus are high. The main purpose of carbon fiber is to compound with resin, metal, ceramics and carbon as a reinforcing material to make advanced composite materials.
High-strength, high-modulus fiber with carbon content above 90%. High temperature resistance ranks first among all chemical fibers. It is made of acrylic fiber and viscose fiber as raw materials, after high temperature oxidation and carbonization. It is an excellent material for manufacturing high-tech equipment such as aerospace and aviation.
The main technical parameters
for reference only
The single wire diameter is the same regardless of 1K, 12K or other K numbers, 6.9um.
1K is a bundle composed of 1,000 monofilaments, and 12K is a bundle composed of 12,000 monofilaments. Temperature resistance 2-3000 degrees.
The resistance values of carbon fiber yarn 3K6K12K24K are: 144 ohm/meter, 72 ohm/meter, 36 ohm/meter, 18 ohm/meter.
3K, 6K: tensile strength: 3530Mpa, tensile modulus: 230Gpa, elongation: 1.5%, density: 1.76g/cm3.
12K.24K: Tensile strength: 4900Mpa, tensile modulus: 230Gpa, elongation: 2.1%, density: 1.80g/cm3
for reference only
The single wire diameter is the same regardless of 1K, 12K or other K numbers, 6.9um.
1K is a bundle composed of 1,000 monofilaments, and 12K is a bundle composed of 12,000 monofilaments. Temperature resistance 2-3000 degrees.
The resistance values of carbon fiber yarn 3K6K12K24K are: 144 ohm/meter, 72 ohm/meter, 36 ohm/meter, 18 ohm/meter.
3K, 6K: tensile strength: 3530Mpa, tensile modulus: 230Gpa, elongation: 1.5%, density: 1.76g/cm3.
12K.24K: Tensile strength: 4900Mpa, tensile modulus: 230Gpa, elongation: 2.1%, density: 1.80g/cm3
Packing: 1PC
Warranty period: 120 day
Warranty period: 120 day