3M Scotch-Weld Urethane Adhesive DP620NS, Black, 1.64 fl. oz. (48.5 mL) Duo-Pak

• 3M Scotch-Weld Urethane Adhesive DP620NS is a flexible, two-part polyurethane based structural adhesive that performs well in numerous applications where some flexibility is needed. It effectively bonds to many substrates such as composites, metals, wood, and many plastics and rubbers, ceramics and glass (may require primer for durability).
• Features
  • Ideal choice for bonding dissimilar substrates
  • Non-sagging after dispensing so adhesive stays where placed
  • Low temperature flexibility and low shrinkage
  • Long open time provides ample opportunity to position and adjust work
  • 3M Scotch-Weld Urethane Adhesive DP620NS is a flexible, two-part polyurethane based structural adhesive that performs well in numerous applications where some flexibility is needed. It effectively bonds to many substrates such as composites, metals, wood, and many plastics and rubbers, ceramics and glass (may require primer for durability).
  • When using a Duo-Pak (DP) size adhesive, rely on 3M dispensing equipment (PDF, 1.88 Mb) for convenient and accurate metering, mixing and dispensing
• Specifications
  • Part No.: 96416
  • Product Line: MMM
  • MFR Model: 96416
  • Standard/Approvals: California Pro65 Warning: Cancer and Reproductive Harm | CONEG Complied | Conflict Minerals Regulation | CPSIA 2008 | EU REACH | EU RoHS Compliant | GADSL
  • Applications: For transportation applications, bonding wood, metal or composite door frames to wood or other surfaces, bonding wood paneling to wood or plaster, sealing fabric water hoses, encapsulating for tamper-proofing, flexible plastic or composite bonding
  • Manufacturer: 3M Products
  • Alternate Part Number-1: 62264550302
  • UPC: 021200964169
  • Brand: Scotch-Weld
  • Applicable Materials: Ceramic, Glass, Hardboard, Metal, Plastic, Rubber, Wood
  • Composition: 30 to 60% P,P'-Methylenebis(Phenyl Isocyanate), 15 to 40% 4,4'-Diisocyanatodiphenylmethane Polymer, 15 to 40% Diphenylmethanediisocyanate Prepolymer, <= 1 Silane Ester Derivative, <=0.5% Carbon Black, 0.3% Chromium Compound 1, <0.1% Chromium Compound 2, <0.1% Chromium Compound 3, <0.02% Chromium (Part A)/20 to 50% Polyether Polyol, 15 to 40% Propoxylated Trimethylolpropane, 1 to 10% Amorphous Silica, 1 to 10% 1-4-Cyclohexanedimethanol, 0.1 to 5% Aluminum Oxide, 0.1 to 5% Calcium Oxide, 0.1 to 5% Isophorone Diamine, 0.1 to 5% Potassium Oxide, <= 1% Sodium Oxide, <= 0.5% m-Xylene-Alpha,Alpha'-Diamine (Part B)
  • Application Time: 20 min
  • Specific Gravity: 1.11 (Part A), 1 to 1.2 (Part B)
  • Base Type: Polyurethane
  • Component: 2K
  • Odor/Scent: Low/No Detectable (Part A), Slight Ammonia (Part B)
  • Color: Black (Part A), Milky White (Part B)
  • Container Size (mL): 50
  • Setting Time: 4 hr
  • Flash Point: 290 deg F
  • Container Type: Duo Pack Syringe
  • Form: Viscous
  • Series: DP620NS
  • Temperature Rating (deg F): 60 to 80
  • Type: 2-Part, Structural
  • Curing Time: 48 hr
• Part Number DP620NS, 3M ID 62264535352, UPC 048011572871