Premium
Tinted Epoxy PT105 is an industrial grade epoxy coating material for high
performance floors. The product has
various applications due to its excellent mechanical, chemical, electrical and
adhesion properties to most substrates.
Two
components (A & B) comes in tinted, 100% solid epoxy used as basecoat,
primer or tinted finish surface, with chemical resistance and durability, ideal
for variety of floor coating systems.
Premium Tinted Epoxy PT105 is a high-quality solvent-less, odorless two
component coating system for concrete surfaces such as driveways, pathways,
workshops and warehouses providing a tough clear film, high gloss and wet look
to protect surface from stains, spills and wear. Premium Tinted Epoxy PT105 has been developed
specifically for Australian conditions using the latest epoxy technology. It provides excellent protection against
weathering conditions and the splash and spillage of a wide range of chemicals. Premium Tinted Epoxy PT105 provides a highly
durable, chalk resistant, wear and chemical resistance surface for concrete
floors. High quality epoxy floor coating system in many colours that is solvent
free when used as coating or binder. The product can be tinted in all Australian Standard Colours. Tinted
Epoxy coating has specially developed to be incorporated with non-slip
materials and a large number of decorative materials to provide your desired
floor finishing system, with functionality and style. The surface may be laid as a thin film using
roller applicator. The thickness of the
coating can be reduced by addition of Diluent.
Aggregates may be added to the surface (while wet) to create a non-slip
flooring finish.
Typical Applications
§ Workshops
§ Warehouses
§ Swimming Pools
§ Pharmaceutical Industries
§ Amenity Blocks
§ Food Processing Plants
§ Dairy Industries
§ Loading Docks
§ Laundry Facilities
§ Bakeries and Food Outlets
§ Steelwork Coating
§ Garage and Carparks
Premium
Tinted Epoxy PT105 is supplied in two pack kit, Part A (Resin) and Part B
(Curative or Hardener). Other parts such
as pigment, flakes, decorative and non-slip materials can be supplied
separately. Selected features of Tinted
Epoxy Premium 105TP:
§ Modern, Hygiene, Functional and Economical.
§ Heavy duty clear or pigmented coating for concrete and polished
concrete floors.
§ Highly resistant to chemical attack and pedestrian or vehicular
traffic.
§ Can be used in conjunction with graded aggregates to produce durable
decorative floor finishes.
§ Long lasting and easily maintained with good resistance to a wide
range of domestic and commercial chemicals.
§ Solvent free when used as a clear un-pigmented coating or binder.
§ Outstanding water resistance.
§ Seamless, easy to clean and maintain.
§ Suitable for Flake Flooring systems, see SHIMI FLAKE flooring
system.
§ Superior Chemical Resistant Finished surface
§ Excellent UV stability
§ Solvent Free (Unless you apply Diluent for thickness control)
§ Engineered formulation for trafficable area with high mechanical
strength
§ DIY Friendly, easy to apply and curable over a wide range of
temperature
§ Available with a wide range of Flakes for decorative concrete
§ Ideally compatible for Non-Slip Flooring System.
§ Modern, hygienic, functional and economical.
First coat usually consumes
more and the second coat less.
Standard Colours:
§ White N14
§ Black N61
§ Neutral Grey N23
§ Dark Grey N64
§ Cream Y34
§ Charcoal B64
§ Terracotta R52
§ Bright Blue B23
§ Dark Brown X65
SHIMICOAT
offers all Australian Standard AS2700 Colours, consisting of 206 colours.
Please contact SHIMICOAT office for your custom design tint. Extra charges may
apply.
Roller,
Brush or Squeegee.
|
45 minutes at 25°C |
|
|
Tack Free: |
2-3 hours |
|
Thin Film Set: |
8 Hours (Min, depending on temperature and humidity) |
|
Dry Cured: |
12-24 hours – Foot Traffic (depending on temperature and humidity) |
|
Fully Cured: |
7 days (Vehicle Traffic) |
|
Re-Coat: |
Over night |
Thinner
& Diluent (Blend of Solvents).
Clean
and dry surface. Ensure surface to be coated is free of all dirt, grease, oil, paint,
curing agents and other contaminants. Removal of Oil
Contamination by degreaser and alkaline cleaning pressure wash
Acid-wash
to enhanced surface porosity and etch the surface. Ensure moisture free surface. Allow to completely dry, run Dry
Test. Place a piece of plastic over a
small area, tape the edges and leave for 1 hour. Remove plastic, if there is no moisture on
either surface, concrete is sufficiently dry. Ideally, always consider surface grinding and
removal of loose materials. Grinding is always advisable prior to application of all Shimicoat Epoxy
products, to maximize adhesion. For further information, please refer to SHIMICOAT Instruction for
“Surface Preparations”.
Physical &
Chemical properties of Tinted Epoxy Premium 105TP:
|
Mix Ratios |
3A:1B (Volume) or 4.5A:1B
(Weight) For Example: 3Lt of A (4.5Kg) & 1Lt of B (1Kg) |
|
Pot Life @25°C |
45min |
|
Colour of Blend |
Available in All Australian Standard AS 2700 Colours |
|
Specific Gravity (SG) of Blend |
1.4 |
|
Low Profile Coverage (Kg/sqm) |
Roller Application (200micron) - 0.2Kg of Blend per sqm |
|
Maximum Temperature Surface Exposure (°C) |
140 |
|
Initial Cure Time (Hours) |
24Hours |
|
Ultimate Cure Time (Days) |
7 Days |
|
Compressive strength (ASTM D 695-85) |
>70 |
|
Tensile strength (ASTM D 638-86) |
>15 |
|
Flexural strength (ASTM D 790-86) |
>15 |
|
Hardness shore D (ASTM D2240-86) |
>81 |
|
Abrasion Resistance (ASTM D4060-90) |
0.056 g/1000 cycle |
|
Media |
Reagent |
Rating |
||
|
Acids |
Hydrochloric Acid |
B |
||
|
Sulphuric Acid |
C |
|||
|
Acetic Acid |
B |
|||
|
Nitric Acid (10% max) |
C |
|||
|
Phosphoric Acid (25% max) |
B |
|||
|
Alkalis |
Sodium Hydroxide |
B |
||
|
Ammonium Hydroxide |
A |
|||
|
Potassium Hydroxide |
B |
|||
|
Sodium Hypochlorite (Bleach) |
A |
|||
|
Solvents |
Xylene |
A |
||
|
Methyl Ethyl Ketone (MEK) |
C |
|||
|
Diesel |
A |
|||
|
Ethanol |
A |
|||
|
Acetone |
B |
|||
|
Kerosene |
A |
|||
|
Petrol |
A |
|||
|
Wine & Beer |
A |
|||
|
Code |
Resistance |
Description |
||
|
A |
Excellent |
Suitable for Long
term immersion |
||
|
B |
Good |
Suitable for
Short-term immersion (Max 3 days) |
||
|
C |
Caution |
Very short contact
time is OK, spill and splash |
||
|
D |
Danger |
Not Recommended |
||
|
Indicative reference only.
Tested in laboratory conditions at 25°C. |
||||
Resistance
properties of Tinted Epoxy Premium 105TP:
|
Heat Resistant |
140°C |
Alkalis |
Resist Short term
immersion in all alkalis. |
|
Weather
Proofing |
All Epoxy Coatings
may yellow with time. Weatherproof top
coat may be used if required. |
Salts &
Brines |
Resist continuous
or long-term immersion in all Salts & Brine systems. |
|
Solvents |
Resistant to most
hydrocarbon solvents and alcohols. |
Water |
Excellent resist
to continuous or long term immersion in fresh & Salt Water. |
|
Acids |
Resist splash and
spills in all acids. |
Abrasion |
Excellent when
fully cured (7 Days) |
Mix thoroughly for a minimum 3 minutes
manual or with mechanical mixer at low speed (750rmp Max).
If mixing smaller portions mix at a ratio of
3A:1B by volume. For example, to prepare 2Lt mix, add 500mL of Part B into
1.5Lt of Part A.
§ Ensure surface to be coated is dry, moisture can cause blooming and
delamination.
§ Pot life is approximately 45 minutes, work within 30min to ensure
easy flow application.
§ SHIMI COLOURS, SHIMI METALLIC or SHIMI GLITTERS should be first
added to Part A (Resin). Mix slowly
using drill mixer on low speed. Mix for
a few minutes to ensure completely homogenized without lump. Pour the bend into your tray and apply
directly on the surface using the roller.
§ Use steady long strokes and avoid overworking the roller or pushing
your roller too quickly as this may trap air bubbles in the coating.
§ Do not apply if the rain is expected within 24 hours of application.
§ New concrete should be allowed to cure fully (at least 28days)
before application.
§ Keep the pail sealed when not in use. Avoid application on hot
surfaces.
|
Temp °C |
Pot Life
(min) |
Surface
Dry (Hours) |
Initial
Cure (Hours) |
Recoat
Time (Hours) |
Fully
Cured (Days) |
|
10°C |
45 |
12 |
24 |
24 |
7 Days |
|
20°C |
40 |
10 |
18 |
18 |
7 Days |
|
30°C |
35 |
8 |
16 |
16 |
7 Days |
Premium
Tinted Epoxy PT105 cures in 8-16 hours at 25°C. High temperatures and windy conditions may
speed the curing time. Keep foot traffic
off the final coat for at least 16 hours and vehicles for at least 7 days. Full
hardness is achieved after 7 days.
WARNING
§ Heavy vehicles with hot tires may cause damage on driveway. Avoid
driving over the new coated floors till completely cured (7 Days). For parking the car, place a mat under each
tire during the first few weeks to ensure longevity of your new floor.
§ Do not apply Tinted Epoxy Premium 105TP, if the concrete has a
patchy appearance as moisture may be present. Dry Test prior to application.
§ Direct sunlight and UV radiation my result in chalking, colour
variations and yellowing effect over time.
UV resistance topcoat shall be used.
The products shall be stored out of direct
sunlight and heat at all times. The
shelf life of the product is 24 months, mix uniformly for 3 minutes prior to
use.
DISCLAIMER
Material Safety Data Sheet,
Technical and Environmental Data Sheet can be provided upon request.
The
information provided in this document is guidance only and considering the uses
of this product are beyond the seller's control, the product is sold without
guarantees or warranties. Warranties and
guarantees shall be governed by SHIMICOAT Standard Terms of Sale. The purchaser shall make its own tests to
determine the suitability for their specific application, and Shimicoat Pty Ltd
is taking no responsibility for misuse of the product. The purchaser assumes
all risk of use and handling of this product. This product will be happily
replaced or credited back if defective.
Beyond this, Shimicoat Pty Ltd is not liable for any damages caused by
this product or its use. This information and all further technical
advice are based on our present knowledge and experience.
The customer is not released from the
obligation to conduct careful inspection and testing of supplied goods.